|Body/Hex Nut/Push Nut/Holder/Cover/Gland Nut||Copper Alloy|
|Metal Ball / Spring||SUS|
|Contacts||Copper Alloy With Au Plating|
|Visual and Dimensional Inspection||Must meet or exceed the requirements specified by the most current version of the GT2611 Specification.|
|Insulation Resistance||DC500V±10%‚ test for 1 minute and the insulation resistance should be more than 100MΩ|
|Withstanding Voltage||650 VAC between contacts ， 650 VAC between contacts and metal-housing， for 1±5s min.|
|Contact Resistance||10mΩ at 10mA Max.|
|Pin Pull Test||1. Initial: 24 N minimum.
2. After Test: 16 N minimum.
|Durability||2000 cycles insertion/extraction cycles at a maximum rate of 200cycles per hour.|
|Physical Shock||No discontinuities of 1 μs or longer duration when mated are subjected to 11 ms duration 30 Gs half-sine shock pulses. Three shocks in each direction applied along three mutually perpendicular planes for a total of 18 shocks.|
|Random Vibration||The electrical load conditions shall be 100mA maximum for all contacts.
Frequency: 50 to 2000 Hz
PDS: 0.04 g? /Hz.
Duration: 1 Hour/Axis， 3 Axes Total.
g’s: 7.56 g rms
|Thermal Shock||5 cycles at -40° / +105°， after the test， the function and appearance can't be impacted.|
|Humidity Life||96 hours minimum (seven step cycles).|
|Salt Spray||The test liquid (Nacl) thickness is 5%， Compressing the air pressure is 0.083Mpa， Spraying amount is 1~2 ml/80cm/h， Temperature of the pressure barrel is 43°， LAB temperature is 35°， relative humidity of LAB is 95%~98%， test time is 48hours， after the test， check if there is rusty and oxidized phenomenon.|
|Waterproof Test||Submersion in water 1 meter for 24 hours.|
|Temperature Life||85° for 48Hours Method A， Mated|
|Cycling Humidity||4 cycles at 25° / +85° 95%RH (1 cycles/day)|
|UV Exposure||24Hr equal 1 year: Total require 3 years
8h UV at 70 (±3) ° Black Panel Temperature
4h Condensation at 50 (±3) ° Black Panel Temperature